The aim of this work is the analysis of the hot dip zinc coated steel plates mechanical properties by means of a traditional four-point bending test, performed on coated specimens at three different bending angles. Results are analysed both in terms of mechanical behaviour and phase damages of coatings. The influence of the chemical composition of zinc baths is correlated to intermetallic phase formation and their damages. It is found that, depending on the bath composition, the different phases can form in different amounts, influencing the mechanical behaviour of the coating.
Bath chemical composition influence on intermetallic phases damage in hot dip galvanizing
Bellini C.;Di Cocco V.;Iacoviello F.;Mocanu L. P.
2021-01-01
Abstract
The aim of this work is the analysis of the hot dip zinc coated steel plates mechanical properties by means of a traditional four-point bending test, performed on coated specimens at three different bending angles. Results are analysed both in terms of mechanical behaviour and phase damages of coatings. The influence of the chemical composition of zinc baths is correlated to intermetallic phase formation and their damages. It is found that, depending on the bath composition, the different phases can form in different amounts, influencing the mechanical behaviour of the coating.File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
1-s2.0-S2452321622003444-main.pdf
accesso aperto
Tipologia:
Versione Editoriale (PDF)
Licenza:
Creative commons
Dimensione
2.32 MB
Formato
Adobe PDF
|
2.32 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.