Gadolinium (10%)-doped ceria was successfully synthesized by using an urea-based co-precipitation method (UBHP). A single fluorite phase was obtained after a low temperature (400 °C) calcination treatment. The resulting powders showed grains of nanometric size with some agglomerations and an overall good sinterability. Pellets were sintered at 1300 and 1500 °C for 3 h. The ionic conductivity was measured by electrochemical impedance spectroscopy measurements and a correlation between electrical properties and microstructure was revealed. The promising conductivity values showed that the synthesized powders are suitable for intermediate temperature solid oxide fuel cells (IT-SOFCs) applications.

Gadolinium-doped ceria nanopowders synthesized by urea-based homogeneous co-precipitation (UBHP)

SPIRIDIGLIOZZI, Luca;DELL'AGLI, Gianfranco
2017-01-01

Abstract

Gadolinium (10%)-doped ceria was successfully synthesized by using an urea-based co-precipitation method (UBHP). A single fluorite phase was obtained after a low temperature (400 °C) calcination treatment. The resulting powders showed grains of nanometric size with some agglomerations and an overall good sinterability. Pellets were sintered at 1300 and 1500 °C for 3 h. The ionic conductivity was measured by electrochemical impedance spectroscopy measurements and a correlation between electrical properties and microstructure was revealed. The promising conductivity values showed that the synthesized powders are suitable for intermediate temperature solid oxide fuel cells (IT-SOFCs) applications.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11580/59232
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 38
social impact