Nanocrystalline 20mol% samaria-doped ceria powders (Ce0.8Sm0.2O1.9) were synthesized by coprecipitation techniques using various precipitating agents in aqueous solution: ammonia, ammonium carbonate, tetramethylammonium hydroxide, and urea. The synthesized powders after calcination at 600∘C possess a fluorite structure with nanometric size although they are characterized by a very different morphology and degree of agglomeration. Remarkable differences appear in the sintering behavior, especially because of the presence of hard agglomerates. The precipitating agent has therefore a crucial role in the coprecipitation process, which influences the morphology of the powders and in turn the sintering behavior. The obtained results clearly reveal that ammonium carbonate and urea are the best precipitating agents to obtain final dense products after sintering.

Effect of the Precipitating Agent on the Synthesis and Sintering Behavior of 20 mol% Sm-Doped Ceria

SPIRIDIGLIOZZI, Luca;DELL'AGLI, Gianfranco
;
PANSINI, Michele
2016-01-01

Abstract

Nanocrystalline 20mol% samaria-doped ceria powders (Ce0.8Sm0.2O1.9) were synthesized by coprecipitation techniques using various precipitating agents in aqueous solution: ammonia, ammonium carbonate, tetramethylammonium hydroxide, and urea. The synthesized powders after calcination at 600∘C possess a fluorite structure with nanometric size although they are characterized by a very different morphology and degree of agglomeration. Remarkable differences appear in the sintering behavior, especially because of the presence of hard agglomerates. The precipitating agent has therefore a crucial role in the coprecipitation process, which influences the morphology of the powders and in turn the sintering behavior. The obtained results clearly reveal that ammonium carbonate and urea are the best precipitating agents to obtain final dense products after sintering.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11580/59214
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 32
social impact