Fracture of BCC metals is a temperature dependent process characterized by a temperature transition regime where material failure is the result of the competing action of two different mechanisms of rupture, namely, cleavage and ductile fracture. In this paper, two micromechanics based methodologies, the local approach and a non-linear CDM model, are used to model fracture processes in the temperature transition regime for a low alloy steel. The study revealed that approaching the nihil ductility temperature (NDT), the identification procedure for the material parameters needed in the local approach becomes no longer stable resulting in a non unique set of rW and m values. This occurrence can be used to discriminate in the experimental data set those data failed in a non-complete brittle manner. Using m exponent equal to 4, a linear dependency, between rW and KJ, also in upper shelf regime, is demonstrated

Investigation on the Weibull parameters identification for local approach application in the ductile to brittle transition regime

BONORA, Nicola;GENTILE, Domenico
2007-01-01

Abstract

Fracture of BCC metals is a temperature dependent process characterized by a temperature transition regime where material failure is the result of the competing action of two different mechanisms of rupture, namely, cleavage and ductile fracture. In this paper, two micromechanics based methodologies, the local approach and a non-linear CDM model, are used to model fracture processes in the temperature transition regime for a low alloy steel. The study revealed that approaching the nihil ductility temperature (NDT), the identification procedure for the material parameters needed in the local approach becomes no longer stable resulting in a non unique set of rW and m values. This occurrence can be used to discriminate in the experimental data set those data failed in a non-complete brittle manner. Using m exponent equal to 4, a linear dependency, between rW and KJ, also in upper shelf regime, is demonstrated
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11580/13184
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 14
social impact