A coprecipitated xerogel having the composition of 90 vol.% zirconia (3 mol% Y2O3) and remaining 10 vol.% alumina was crystallized under hydrothermal conditions by adopting conventional (110 °C for 7 days) or microwave (250 °C for 2 h) routes. The hydrothermal treatments of crystallization were performed in the presence of (KOH+K2CO3) (K), (CH3)4NOH (TMA), or (C2H5)4NOH (TEA) mineralizer solutions at different concentrations. The role of the two different hydrothermal routes, of the nature and the concentration of the mineralizer solution on the thermal behaviour of the resulting powders are discussed
Hydrothermal synthesis of precursors for Y-TZP/Al2O3 composite
DELL'AGLI, Gianfranco;MASCOLO, Maria Cristina;MASCOLO, Giuseppe
2004-01-01
Abstract
A coprecipitated xerogel having the composition of 90 vol.% zirconia (3 mol% Y2O3) and remaining 10 vol.% alumina was crystallized under hydrothermal conditions by adopting conventional (110 °C for 7 days) or microwave (250 °C for 2 h) routes. The hydrothermal treatments of crystallization were performed in the presence of (KOH+K2CO3) (K), (CH3)4NOH (TMA), or (C2H5)4NOH (TEA) mineralizer solutions at different concentrations. The role of the two different hydrothermal routes, of the nature and the concentration of the mineralizer solution on the thermal behaviour of the resulting powders are discussedFile in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.