(Ba, Sr)-exchanged zeolite A with composition Ba0.74Sr0.22Na0.04Al2Si2O8 was prepared by cation exchange; a mild thermal treatment converts into an amorphous phase. Successive crystallization and sintering behavior was studied by XRD, DTA, and thermodilatometric analysis. The results point out the activation of viscous flow sintering mechanisms between 900°C and 1050°C. The densification process starts when the amorphous phase reaches its glass transition temperature (897°C) and finishes when the material crystallizes forming hexacelsian. The application of an external pressure in such temperature range allows to achieve an almost complete densification, the material transforming at 1300°C into dense monoclinic celsian much below the typical processing temperature.

Sintering behavior of Ba/Sr celsian precursor obtained from zeolite-A by ion-exchange method

SPIRIDIGLIOZZI, Luca;MAROCCO, Antonello;DELL'AGLI, Gianfranco;PANSINI, Michele
2017-01-01

Abstract

(Ba, Sr)-exchanged zeolite A with composition Ba0.74Sr0.22Na0.04Al2Si2O8 was prepared by cation exchange; a mild thermal treatment converts into an amorphous phase. Successive crystallization and sintering behavior was studied by XRD, DTA, and thermodilatometric analysis. The results point out the activation of viscous flow sintering mechanisms between 900°C and 1050°C. The densification process starts when the amorphous phase reaches its glass transition temperature (897°C) and finishes when the material crystallizes forming hexacelsian. The application of an external pressure in such temperature range allows to achieve an almost complete densification, the material transforming at 1300°C into dense monoclinic celsian much below the typical processing temperature.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11580/64818
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 12
social impact