Five different samples of (Ba, Sr)-exchanged zeolite A, exhibiting the same Na residual content within the experimental error, were prepared by cation exchange. These powders, with or without a previous thermal treatment, were cold pressed in an isostatic press to manufacture cylindrical compacts. Such compacts were subjected to various thermal cycles up to 1500 °C. The sintering and densification of these compacts was studied by determining linear shrinkages, mass variation, bulk density and porosity. All the compacts produced were totally composed by BaAl2Si2O8-SrAl2Si2O8 solid solutions occurring in the polymorph known as monoclinic celsian. Porosity lower than 0.1 % and bulk density higher than 95 % theoretical density were obtained. The problems arising in the sintering of compacts manufactured with zeolitic precursor are discussed and proper measures to solve them are suggested.

Sintering behaviour of celsian based ceramics obtained from the thermal conversion of (Ba, Sr)-exchanged zeolite A

MAROCCO, Antonello;DELL'AGLI, Gianfranco;PANSINI, Michele
2011-01-01

Abstract

Five different samples of (Ba, Sr)-exchanged zeolite A, exhibiting the same Na residual content within the experimental error, were prepared by cation exchange. These powders, with or without a previous thermal treatment, were cold pressed in an isostatic press to manufacture cylindrical compacts. Such compacts were subjected to various thermal cycles up to 1500 °C. The sintering and densification of these compacts was studied by determining linear shrinkages, mass variation, bulk density and porosity. All the compacts produced were totally composed by BaAl2Si2O8-SrAl2Si2O8 solid solutions occurring in the polymorph known as monoclinic celsian. Porosity lower than 0.1 % and bulk density higher than 95 % theoretical density were obtained. The problems arising in the sintering of compacts manufactured with zeolitic precursor are discussed and proper measures to solve them are suggested.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11580/18938
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 30
social impact